Quid est differentia inter overheating et overburning in calor curatio de cast partibus? Quam ut vitare overheating?

I, quod est differentia inter overheating et overburning in cast ferro calor curatio?

Definitio et essentia overheating: refers to the phaenomenon significantly crassum austenite grana in cast ferro propter nimium altum calefacit calor calor aut diu tenementum tempore per calor curatio. In hoc tempore, non est oxidatio vel liquescens intra materiam, nisi abnormes grano structura. Overheating: est a gravius defectus quam overheating, ubi calefacit temperatus excedit ad solidam linea ferro, causing loci liquescens aut oxidatio frumenti terminos et solveret et vim inter grana. Macroscopic et microscopicae characteres overheating: Macroscopic: Non est significans mutatio super superficiem ferro et fractura superficiem potest exhibeant grossum frumenti boni (ut a "sugar sicut" fractura superficiei). Microscopic: Austenitititititic grana sunt graviter crassum, forte cum abnormes structurae ut Weibull structuram. Overheating: Macroscopic: Non potest esse cadmiae scale, borks vel rimas super superficiem et fractura superficiem aspera et caret metallicis lumine. Microscopic, ibi sunt metus marcas, cadmiae inclusions, et etiam grano terminus fregit ad frumenti terminos. Et impulsum in perficientur est overheating: quod potest facere levi decrementum in ferro fortitudinem et duritiam, a significant decrementum in plasticity et lenta et a significant decrescit in impulsum lenta. -Overheating: gravi depravatione mechanica proprietatibus ferro, fere plenus damnum virtutis et plasticity, materia in fragilis et non potest reparari per subsequentem calor curatio. Repackable overheating: per reheating (in normalis temperatus range) et normalizing vel annales curatio, in grano magnitudine potest esse probare et proprietates potest restitui. Overheating: quod est irreversible defectus quod non reparari semel occurs, et materia non solum scrapped.

II, Praecaventur mensuras superiores Phaenomenon in calor curatio de humilis Carbon Steel et Medium Carbon Steel

Minimum Carbon Mede (Carbon Content ≤ 0.25%) et medium ipsum cast ferro (Carbon content 0,25% ~ 0.60%) paulo diversis sensibilibus differentias in calor. Tamen, core idea prohibendi overheating est idem et specifica mensurae sunt, ut sequitur:

I, stricte control calefactio temperatus et tenens tempus ad verius set temperatus range: humilis Carbon Mors: et Austenitizing Temperature solet DCCCL ~ ad ne nimium dissolutionem Ferrite et crassum grano magnitudine). Medium Carbon Mors: et Austenitization Temperature plerumque DCCCXX ~ DCCCLXXX ℃ (nimium potest facere completum dissolution of Pearlite et celeri frumentum incrementum). In operationem practica, necesse est verius monitor in fornacem temperatus per thermocouples secundum crassitiem de castings et moles fornacis loading, ut ne loci overheating. Recte control in time: fundatur in principle "integrum auscinitization et non coarsoening grana", in time tempus est ratione secundum ad effective crassitie de mittentem (plerumque omnis 10mm crassitiem ad mittentem (plerumque omnis 10mm crassitiem ad 30-60 minutes). Cum loading in fornacem, vitare nimia cumulus, ut uniformis calefactio, et reducere loci velocius ad nimium longum.

II, ad optimized calefactio processus adoptat et egressus calefactio modum: nam magna vel universa castings, preheat ad inferiorem temperatus (ut 600-700 ℃ ad redigendum temperatus differentiam accentus ad redigendum per calefacit. Vitare repetita calefactio: multa calefactio potest cumulare periculo crassum grana. Try ad minimize numerum repetita calor treatments pro partibus, et necessitate, inferior secundarium calefacit calor temperatus (10-20 ℃ minus quam primum).

3、 Adjusting process details based on cast steel composition for low-carbon cast steel: Due to poor hardenability, normalizing treatment is often used to refine grains, and the heating temperature should be strictly controlled at 30-50 ℃ above Ac3 (Ac3 is the critical temperature for austenitization, while low-carbon steel is about 830-900 ℃) to avoid blindly raising the temperature in pursuit of hardenability. Medium Carbon Mors Prone ad Weibull compages (Ferrite praecipitatio per austenite grano terminis) post overheating, precise imperium in tellus tempus non requiritur ad integrum dissolutio carbides, sine caeculo parere tempus; Si extinguendo et temperatio curatio est peragatur, quod extinxit calefacit temperatus vitare per "periculo zona" de celeri frumenti incrementum (plerumque 10-30 ℃ minus quam normalizing temperatus).

IV, amplio calefactio apparatu et fornacis installation modi ut uniformis fornacem temperatus: regulariter calibrate temperatus imperium system system calibrae fornacem, et ne loci calidum maculis; Cum calefactio magna items, anti radialis laminis potest esse in solitudinem, seu influunt gubernat cogitationes potest installed in medio fornacis ut sit uniformis temperatus agro. Rationabile fornacis installation: Subsidium sat gap inter castings (plerumque non minus quam 1/3 de mittentem crassitudine) ad vitare stacking et impedimentum; Tenuis et tenuis-muralis components sunt sustentantur verticaliter aut horizontaliter ad redigendum loci calor concentration.

V, confirma processus vigilantia et realis-vicis magna deprehendendi: nam massa-productum castings, primam partem indiget calor curatio, et rationalitate processum est confirmata per metallographic examen (servandis in processus est confirmata per metallographic examen (servandis in processus est confirmata per metallographic examen (servandis in processus est confirmata per metallographic examen (observando grano mole); Ordinarius sampling durante productio ut grano gradu occurrit requisita (plerumque ad gradu V vel supra, cum plura granis ex superioribus gradibus). Recordatio et Tracing: Detailed Recording calefactio temperatus, velit tempus, fornacem load Loading volumen et alia parametri pro fornacem. In casu abnormitates, causa potest cito rationes et processus potest esse adaequatum in opportune modo.

Per supra mensuras, overheating defectus in calor curatio humilis-ipsum et medium ipsum cast ferro potest efficaciter prohiberi, cursus et mechanica proprietates (ut lenta et vires) de castings in occursum consilium requisita.